Influence of cracks on the deterioration mechanisms and durability of reinforced concrete structures
Конференцијски прилог (Објављена верзија)
Метаподаци
Приказ свих података о документуАпстракт
The most important factor that affects concrete deterioration is the appearance of cracks on reinforced concrete (RC) structures, so the influence of loading cracks should not be neglected when the service life is analyzed. For the purposes of this research, reference concrete and concretes with 50% fly ash (FA) and with 100% recycled aggregate (RCA) were prepared. The existing carbonation prediction models were analyzed and modification was proposed in the case of FA and RCA concretes. After establishing the relationship between carbonation resistance and compressive strength, the service life analysis was performed by defining the required concrete cover depth for different concrete types. Samples with 5 different crack widths (0.05, 0.10, 0.15, 0.20 and 0.30mm) and samples without cracks were prepared and subjected to accelerated carbonation. For all concrete types steel stress limitation was pro-posed, which allows the entire service life of RC elements to meet the prescribed requi...rements.
Кључне речи:
durability / cracks / carbonation / fly ash / recycled concrete aggregate / corrosionИзвор:
16th International Congress Proceeding, 2022, 37-46Издавач:
- Association of Structural Engineers of Serbia
Институција/група
GraFarTY - CONF AU - Carević, Vedran PY - 2022 UR - https://grafar.grf.bg.ac.rs/handle/123456789/2724 AB - The most important factor that affects concrete deterioration is the appearance of cracks on reinforced concrete (RC) structures, so the influence of loading cracks should not be neglected when the service life is analyzed. For the purposes of this research, reference concrete and concretes with 50% fly ash (FA) and with 100% recycled aggregate (RCA) were prepared. The existing carbonation prediction models were analyzed and modification was proposed in the case of FA and RCA concretes. After establishing the relationship between carbonation resistance and compressive strength, the service life analysis was performed by defining the required concrete cover depth for different concrete types. Samples with 5 different crack widths (0.05, 0.10, 0.15, 0.20 and 0.30mm) and samples without cracks were prepared and subjected to accelerated carbonation. For all concrete types steel stress limitation was pro-posed, which allows the entire service life of RC elements to meet the prescribed requirements. PB - Association of Structural Engineers of Serbia C3 - 16th International Congress Proceeding T1 - Influence of cracks on the deterioration mechanisms and durability of reinforced concrete structures EP - 46 SP - 37 UR - https://hdl.handle.net/21.15107/rcub_grafar_2724 ER -
@conference{ author = "Carević, Vedran", year = "2022", abstract = "The most important factor that affects concrete deterioration is the appearance of cracks on reinforced concrete (RC) structures, so the influence of loading cracks should not be neglected when the service life is analyzed. For the purposes of this research, reference concrete and concretes with 50% fly ash (FA) and with 100% recycled aggregate (RCA) were prepared. The existing carbonation prediction models were analyzed and modification was proposed in the case of FA and RCA concretes. After establishing the relationship between carbonation resistance and compressive strength, the service life analysis was performed by defining the required concrete cover depth for different concrete types. Samples with 5 different crack widths (0.05, 0.10, 0.15, 0.20 and 0.30mm) and samples without cracks were prepared and subjected to accelerated carbonation. For all concrete types steel stress limitation was pro-posed, which allows the entire service life of RC elements to meet the prescribed requirements.", publisher = "Association of Structural Engineers of Serbia", journal = "16th International Congress Proceeding", title = "Influence of cracks on the deterioration mechanisms and durability of reinforced concrete structures", pages = "46-37", url = "https://hdl.handle.net/21.15107/rcub_grafar_2724" }
Carević, V.. (2022). Influence of cracks on the deterioration mechanisms and durability of reinforced concrete structures. in 16th International Congress Proceeding Association of Structural Engineers of Serbia., 37-46. https://hdl.handle.net/21.15107/rcub_grafar_2724
Carević V. Influence of cracks on the deterioration mechanisms and durability of reinforced concrete structures. in 16th International Congress Proceeding. 2022;:37-46. https://hdl.handle.net/21.15107/rcub_grafar_2724 .
Carević, Vedran, "Influence of cracks on the deterioration mechanisms and durability of reinforced concrete structures" in 16th International Congress Proceeding (2022):37-46, https://hdl.handle.net/21.15107/rcub_grafar_2724 .